Plexiglas? Resist AG 100
Polymethyl Methacrylate Acrylic
PLEXIGLAS? Resist AG 100 is an amorphous thermoplastic molding compound, based on impact-modified polymethyl methacrylate (PMMA).
Properties
PLEXIGLAS? molding compounds have the following typical properties:
PLEXIGLAS? Resist AG 100 is characterized by the following additional properties:
Additive | |
Features | |
Uses | - Automotive Applications，Glazing
|
Appearance | - Clear/Transparent，Transparent Green，Transparent Grey
|
Forms | |
Processing Method | - Coextrusion，Injection Molding，Sheet Extrusion
|
Density | 1.16 | g/cm3 | ISO 1183 |
Melt Volume-Flow Rate (MVR) |
|
| ISO 1133 |
230°C/3.8 kg | 0.0671 | in3/10min |
|
260°C/3.8 kg | 0.470 | in3/10min |
|
Water Absorption |
|
| ISO 62 |
Saturation, 73°F | 1.5 | % |
|
Equilibrium, 73°F, 50% RH | 0.50 | % |
|
Tensile Modulus | 319000 | psi | ISO 527-2/1 |
Tensile Stress (Yield) | 7980 | psi | ISO 527-2/50 |
Tensile Strain (Yield) | 5.0 | % | ISO 527-2/50 |
Nominal Tensile Strain at Break | 45 | % | ISO 527-2 |
Charpy Unnotched Impact Strength (73°F) | 57 | ft·lb/in2 | ISO 179/1eU |
Heat Deflection Temperature |
|
|
|
66 psi, Unannealed | 221 | °F | ISO 75-2/B |
264 psi, Unannealed | 212 | °F | ISO 75-2/A |
Glass Transition Temperature | 234 | °F | ISO 11357-2 |
Vicat Softening Temperature | 221 | °F | ISO 306/B50 |
CLTE - Flow (32 to 122°F) | 6.1E-5 | in/in/°F | ISO 11359-2 |
Flame Rating (0.06 in) | HB |
| IEC 707 |
Refractive Index | 1.490 |
| ISO 489 |
Transmittance 2 | 91.0 | % | ISO 13468-2 |
Haze | 0.70 | % | ASTM D1003 |
Drying Temperature | 158 to 176 | °F |
|
Drying Time | 3.0 to 4.0 | hr |
|
Processing (Melt) Temp | 455 to 518 | °F |
|
Mold Temperature | 140 to 176 | °F |
|
Drying Temperature | 158 to 176 | °F |
|
Drying Time | 3.0 to 4.0 | hr |
|
Melt Temperature | 455 to 518 | °F |
|
Die Temperature | 464 | °F |
|