Radilon? S RV300K 100 NAT
Polyamide 6
PA6 30% glass fiber reinforced injection moulding grade. Heat stabilized. Natural colour.
Suitable for parts requiring medium stiffness, good mechanical resistance and good heat ageing properties retention.
Filler / Reinforcement | |
Additive | |
Features | - Heat Aging Resistant，Heat Stabilized，Medium Stiffness
|
RoHS Compliance | |
Appearance | |
Processing Method | |
Resin ID (ISO 1043) | |
Density | 1.35 | -- | g/cm3 | ISO 1183 |
Water Absorption |
|
|
| ISO 62 |
Saturation, 73°F, 0.0787 in | 7.5 | -- | % |
|
Equilibrium, 73°F, 0.0787 in, 50% RH | 2.0 | -- | % |
|
Tensile Modulus | 1.41E+6 | -- | psi | ISO 527-2/1A/1 |
Tensile Stress (Break) | 24700 | -- | psi | ISO 527-2/1A/5 |
Tensile Strain (Break) | 3.9 | -- | % | ISO 527-2/1A/5 |
Flexural Modulus 3 | 1.12E+6 | -- | psi | ISO 178 |
Flexural Stress 3 | 36300 | -- | psi | ISO 178 |
Charpy Notched Impact Strength |
|
|
| ISO 179/1eA |
-22°F | 5.2 | -- | ft·lb/in2 |
|
73°F | 7.1 | -- | ft·lb/in2 |
|
Charpy Unnotched Impact Strength |
|
|
| ISO 179/1eU |
-22°F | 40 | -- | ft·lb/in2 |
|
73°F | 43 | -- | ft·lb/in2 |
|
Heat Deflection Temperature |
|
|
|
|
66 psi, Unannealed | 419 | -- | °F | ISO 75-2/Bf |
264 psi, Unannealed | 392 | -- | °F | ISO 75-2/Af |
Vicat Softening Temperature | 410 | -- | °F | ISO 306/B50 |
Melting Temperature 4 | 428 | -- | °F | ISO 11357-3 |
Surface Resistivity 5 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
Volume Resistivity 5 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
Comparative Tracking Index(Solution A) | 550 | -- | V | IEC 60112 |
Flame Rating (0.031 in) | HB | -- |
| UL 94 |
Glow Wire Flammability Index (0.08 in) | 1290 | -- | °F | IEC 60695-2-12 |
Flammability (0.12 in) | 0 | -- | in/min | FMVSS 302 |
Drying Temperature - Desiccant Dryer | 176 | °F |
|
Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr |
|
Dew Point - Desiccant Dryer | -4 | °F |
|
Suggested Max Moisture | 0.15 | % |
|
Processing (Melt) Temp | 464 to 536 | °F |
|
Mold Temperature | 176 to 194 | °F |
|
Injection Rate | Moderate-Fast |
|
|