VICTREX CT? POLYMER 100
High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, colour natural.
Applications at very low temperatures. Wear and erosion resistant and chemically resistant to aggressive environments.
Material Properties |
Physical | Nominal Value | Unit | Test Method |
Density (Crystalline) | 1.30 | g/cm3 | ISO 1183 |
Spiral Flow |
|
| Internal Method |
-- 1 | 19.0 | cm |
|
-- 2 | 63.0 | cm |
|
-- 3 | 70.0 | cm |
|
Molding Shrinkage 4 |
|
| ISO 294-4 |
Across Flow | 1.3 | % |
|
Flow | 0.90 | % |
|
Mechanical | Nominal Value | Unit | Test Method |
Tensile Stress |
|
| ISO 527-2 |
Yield, 23°C | 95.0 | MPa |
|
Break, -196°C | 200 | MPa |
|
Tensile Strain |
|
| ISO 527-2 |
Break | 32 | % |
|
Break, -196°C | 8.0 | % |
|
Break, 23°C | 70 | % |
|
Flexural Modulus |
|
| ISO 178 |
-196°C | 5400 | MPa |
|
23°C | 3500 | MPa |
|
Flexural Stress |
|
| ISO 178 |
-196°C | 435 | MPa |
|
23°C | 150 | MPa |
|
3.5% Strain, 23°C | 120 | MPa |
|
Compressive Stress |
|
| ISO 604 |
-196°C | 305 | MPa |
|
23°C | 120 | MPa |
|
Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact Strength | 7.2 | kJ/m2 | ISO 180 |
Hardness | Nominal Value | Unit | Test Method |
Shore Hardness (Shore D, 23°C) | 84.0 |
| ISO 868 |
Thermal | Nominal Value | Unit | Test Method |
Glass Transition Temperature (Onset) | 143 | °C | ISO 11357-2 |
Melting Temperature | 343 | °C | ISO 11357-3 |
CLTE - Flow |
|
|
|
-165°C | 42 | ppm/K | DIN 51909 |
< 143°C | 45 | ppm/K | ISO 11359-2 |
CLTE - Average |
|
| ISO 11359-2 |
< 143°C | 65 | ppm/K |
|
> 143°C | 160 | ppm/K |
|
Thermal Conductivity |
|
|
|
-165°C 5 | 0.15 | W/m/K | Internal Method |
23°C 6 | 0.32 | W/m/K | ISO 22007-4 |
Fill Analysis | Nominal Value | Unit | Test Method |
Melt Viscosity (400°C) | 550 | Pa·s | ISO 11443 |