Ixef? 1022

Manufacturer: SOLVAY
Produced At: Import/ China
Product Category: IXEF PARA
Product No: Ixef 1022
Product Quantity: 25KG / BAG
Product Features: Chemical Resistant，Creep Resistant，General Purpose，Good Dimensional Stability，Good Sterilizability，High Flow，High Strength，Low Moisture Absorption，Outstanding Surface Finish，Ultra High Stiffness

Product information

Ixef? 1022

Polyarylamide

Solvay Specialty Polymers

Product Description:

Ixef? 1022 is a 50% glass-fiber reinforced, general purpose polyarylamide compound that exhibits very high strength and rigidity, outstanding surface gloss, and excellent creep resistance.

Filler / Reinforcement	Glass Fiber, 50% Filler by Weight
Features	Chemical Resistant，Creep Resistant，General Purpose，Good Dimensional Stability，Good Sterilizability，High FlowHigh Strength，Low Moisture Absorption，Outstanding Surface Finish，Ultra High Stiffness
Uses	Appliances，Automotive Applications，Automotive Interior Parts，Cell Phones，Electrical PartsFurniture，High Gloss Applications，Hospital Goods，Medical Devices，Sporting Goods，Surgical Instruments
RoHS Compliance	RoHS Compliant
UL File NumberGlobal	E95746
Appearance	Black，Colors Available，Natural Color
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.64	--	g/cm3	ISO 1183
Molding Shrinkage	0.10 to 0.30	--	%	ISO 294-4
Water Absorption (73°F, 24 hr)	0.16	--	%	ISO 62
Moisture Absorption - Equil, 65% RH	1.50	--		Internal Method

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	2.90E+6	2.90E+6	psi	ISO 527-2
Tensile Stress (Break)	40600	37700	psi	ISO 527-2
Tensile Strain (Break)	1.9	2.2	%	ISO 527-2
Flexural Modulus	2.76E+6	--	psi	ISO 178
Flexural Stress	58000	--	psi	ISO 178
Impact	Dry	Conditioned	Unit	Test Method
Notched Izod Impact	2.1	--	ft·lb/in	ASTM D256
Unnotched Izod Impact	16	--	ft·lb/in	ASTM D256

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature (264 psi, Unannealed)	446	--	°F	ISO 75-2/A
CLTE - Flow	8.3E-6	--	in/in/°F	ISO 11359-2

Electrical	Dry	Conditioned	Unit	Test Method
Volume Resistivity	1.0E+13	--	ohms·cm	IEC 60093
Electric Strength	790	--	V/mil	IEC 60243-1
Dielectric Constant (110 Hz)	4.60	--		IEC 60250
Comparative Tracking Index	570	--	V	IEC 60112
Dissipation Factor	0.017	--		IEC 60250
Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating 3	HB	--		UL 94
Oxygen Index	25	--	%	ISO 4589-2

Injection	Dry	Unit
Drying Temperature	248	°F
Drying Time	0.50 to 1.5	hr
Rear Temperature	482 to 500	°F
Front Temperature	500 to 554	°F
Nozzle Temperature	500 to 554	°F
Processing (Melt) Temp	536	°F
Mold Temperature	248 to 284	°F
Injection Rate	Fast
Injection Notes
Hot runners: 250°C to 260°C (482°C to 500°F) Storage Ixef? compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Ixef? resins be dried prior to molding following the recommendations found in this datasheet and/or in the Ixef? processing guide. Drying The material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F). Injection Molding Ixef 1022 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The measured melt temperature should be about 280°C (536°F), and the barrel temperatures should be around 250 to 260°C (482 to 500°F) in the rear zone, gradually increasing to 260 to 290°C (500 to 554°F) in the front zone. If hot runners are used, they should be set to 250 to 260°C (482 to 500°F). To maximize crystallinity, the temperature of the mold cavity surface must be held between 120 and 140°C (248 and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95-99%).