Radilon? S LRV300LUK 100 NAT
聚酰胺6
PA6 30% glass fiber reinforced injection moulding grade. Lubricated, high flowability. Improved UV resistance. Natural colour.
Suitable for parts requiring high stiffness and good mechanical resistance, which must also resist to outdoor exposure.
ISO 1043 : PA6-T GF30
填料/增強材料 | |
添加劑 | |
特性 | |
RoHS 合規性 | |
外觀 | |
加工方法 | |
樹脂ID (ISO 1043) | |
密度 | 1.35 | -- | g/cm3 | ISO 1183 |
吸水率 |
|
|
| ISO 62 |
飽和, 73°F, 0.0787 in | 7.5 | -- | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 2.0 | -- | % |
|
拉伸模量 | 1.39E+6 | 928000 | psi | ISO 527-2/1A/1 |
拉伸應力 (斷裂) | 26100 | 16000 | psi | ISO 527-2/1A/5 |
拉伸應變 (斷裂) | 3.4 | 4.5 | % | ISO 527-2/1A/5 |
彎曲模量 2 | 1.29E+6 | -- | psi | ISO 178 |
彎曲應力 2 | 37700 | -- | psi | ISO 178 |
簡支梁缺口沖擊強度 |
|
|
| ISO 179/1eA |
-22°F | 5.2 | -- | ft·lb/in2 |
|
73°F | 6.2 | 9.5 | ft·lb/in2 |
|
簡支梁無缺口沖擊強度 |
|
|
| ISO 179/1eU |
-22°F | 33 | -- | ft·lb/in2 |
|
73°F | 43 | 52 | ft·lb/in2 |
|
熱變形溫度 (264 psi, 未退火) | 392 | -- | °F | ISO 75-2/Af |
維卡軟化溫度 | 410 | -- | °F | ISO 306/B50 |
熔融溫度 3 | 428 | -- | °F | ISO 11357 |
表面電阻率 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
體積電阻率 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
漏電起痕指數 | 600 | -- | V | IEC 60112 |
燃燒速率 | 0.0 | -- | in/min | FMVSS 302 |
UL 阻燃等級 (0.031 in) | HB | -- |
| UL 94 |
灼熱絲易燃指數 (0.08 in) | 1290 | -- | °F | IEC 60695-2-12 |
干燥溫度 - 熱風干燥機 | 176 | °F |
|
干燥時間 - 熱風干燥機 | 2.0 到 4.0 | hr |
|
Dew Point - 熱風干燥機 | < -4 | °F |
|
建議的最大水分含量 | 0.15 | % |
|
加工（熔體）溫度 | 464 到 536 | °F |
|
模具溫度 | 176 到 194 | °F |
|
注射速度 | 中等偏快 |
|
|