VESTAMID? Care ML94
聚酰胺12
VESTAMID?Care ML grades cover a range of polyamide 12 resins of different viscosity for processing via extrusion or injection molding. The VESTAMID?Care ML product range consists of unstabilized base resins as well as stabilized or reinforced compounds.
VESTAMID? Care ML resins are characterized by several outstanding properties, such as high impact & notched impact resistance, dimensional stability, good sliding properties, high abrasion resistance and resistance against chemicals.
Unfilled VESTAMID? Care ML grades are for example the materials of choice for catheters and tubings, where VESTAMID? Care ML materials meet even highest challenges in applications such as angioplasty balloon catheters.
Typical areas of application for reinforced VESTAMID? Care ML grades include housing-parts, monitoring and imaging devices and durable medical equipment. Due to their low water uptake, filled VESTAMID? Care ML grades even resist steam autoclaving for more than 500 cycles. The advantages at a glance :
特性 | |
用途 | - 管件、醫(yī)療/護(hù)理用品、醫(yī)療器械
|
機構(gòu)評級 | - ISO 10993、USP 88、USP 第VI類
|
加工方法 | |
密度 (73°F) | 1.01 | g/cm3 | ISO 1183 |
收縮率 |
|
| ISO 294-4 |
橫向流量 : 0.0787 in | 1.2 | % |
|
流量 : 0.0787 in | 0.85 | % |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F | 1.5 | % |
|
平衡, 73°F, 50% RH | 0.80 | % |
|
拉伸模量 | 196000 | psi | ISO 527-2 |
拉伸應(yīng)力 (屈服, 73°F) | 6530 | psi | ISO 527-2 |
拉伸應(yīng)變 (屈服, 73°F) | 5.0 | % | ISO 527-2 |
標(biāo)稱拉伸斷裂應(yīng)變 (73°F) | > 50 | % | ISO 527-2 |
簡支梁缺口沖擊強度 |
|
| ISO 179/1eA |
-22°F, 完全斷裂 | 2.9 | ft·lb/in2 |
|
73°F, 完全斷裂 | 2.9 | ft·lb/in2 |
|
簡支梁無缺口沖擊強度 |
|
| ISO 179/1eU |
-22°F | 無斷裂 |
|
|
73°F | 無斷裂 |
|
|
熱變形溫度 |
|
|
|
66 psi, 未退火 | 248 | °F | ISO 75-2/B |
264 psi, 未退火 | 122 | °F | ISO 75-2/A |
維卡軟化溫度 |
|
|
|
-- | 338 | °F | ISO 306/A |
-- | 284 | °F | ISO 306/B |
溶融溫度（DSC） 2 | 352 | °F | ISO 11357 |
線形熱膨脹系數(shù) - 流動 (73 到 131°F) | 8.3E-5 | in/in/°F | ISO 11359-2 |
可燃性等級 |
|
| IEC 60695-11-10, -20 |
0.06 in | HB |
|
|
0.13 in | HB |
|
|
如需德固賽原廠物性表及相關(guān)文件，請聯(lián)系我們工作人員，謝謝！