ACRYMID 813 compound is an amorphous and heat-resistant thermoplastic molding compound based on polymethyl methacrylimide (PMMI).
Typical properties of ACRYMID? heat-resistant molding compounds are:
The special properties of ACRYMID 813 compound are:
Application:
Used for injection molding parts that involve a high degree of thermal stress.
密度 / 比重 | 1.21 |
| ASTM D792 |
熔流率（熔體流動速率） (260°C/3.8 kg) | 16 | g/10 min | ASTM D1238 |
收縮率 - 流動 | 8.0E-3 到 9.0E-3 | in/in | ASTM D955 |
吸水率 (平衡) | < 0.30 | % | ASTM D570 |
洛氏硬度 (M 級) | 97 |
| ASTM D785 |
拉伸模量 | 595000 | psi | ASTM D638 |
抗張強度 | 13100 | psi | ASTM D638 |
伸長率 |
|
| ASTM D638 |
屈服 | 2.0 到 4.0 | % |
|
斷裂 | 2.0 到 4.0 | % |
|
彎曲模量 | 551000 | psi | ASTM D790 |
彎曲強度 | 19900 | psi | ASTM D790 |
懸壁梁缺口沖擊強度 (73°F, 0.250 in) | 0.25 | ft·lb/in | ASTM D256 |
載荷下熱變形溫度 (264 psi, 退火, 0.250 in) | 252 | °F | ASTM D648 |
維卡軟化溫度 | 259 | °F | ASTM D1525 |
線形熱膨脹系數(shù) - 流動 (32 到 212°F) | 4.3E-5 | in/in/°F | ASTM D696 |
透射率 (126 mil) | 91.0 | % | ASTM D1003 |
霧度 (126 mil) | < 1.0 | % | ASTM D1003 |
黃度指數(shù) (0.126 in) | < 1.0 | YI | ASTM D1925 |
干燥溫度 | 239 | °F |
|
干燥時間 | 2.0 到 3.0 | hr |
|
料筒后部溫度 | 482 到 536 | °F |
|
料筒中部溫度 | 482 到 536 | °F |
|
料筒前部溫度 | 482 到 536 | °F |
|
加工（熔體）溫度 | 482 到 536 | °F |
|
模具溫度 | 176 到 212 | °F |
|
如需德固賽原廠物性表及相關文件，請聯(lián)系我們工作人員，謝謝！