Desmopan? 3690AU
熱塑性聚氨酯彈性體（聚酯）
Extrusion- and injection molding grade; hydrolysis-stabilised; with special UV stabilizers; with release agent; transparent up to 6 mm wall thickness; good wear resistance; Application; Sports shoe soles; Films; Hoses, non-reinforced
添加劑 | |
特性 | |
用途 | |
RoHS 合規性 | |
外觀 | |
加工方法 | |
密度 |
|
|
|
73°F | 1.21 | g/cm3 | ISO 1183 |
-- | 0.0438 | lb/in3 | ISO 1183 2 |
肖氏硬度 |
|
|
|
邵氏 A, 1 秒, 73°F | 91 |
| ISO 7619 |
邵氏 D, 1 秒, 73°F | 40 |
| ISO 7619 |
邵氏 A, 3 sec | 91 |
| ISO 868 2 |
邵氏 D, 15 sec | 40 |
| ISO 868 2 |
拉伸應力 3 |
|
| DIN 53504 |
斷裂, 73°F | 8730 | psi |
|
10% 應變, 73°F | 508 | psi |
|
50% 應變, 73°F | 1160 | psi |
|
100% 應變, 73°F | 1450 | psi |
|
300% 應變, 73°F | 3470 | psi |
|
拉伸應變 3 (斷裂, 73°F) | 510 | % | DIN 53504 |
Tensile Storage Modulus |
|
| ISO 6721 |
-4°F | 136 | ksi |
|
68°F | 13.6 | ksi |
|
140°F | 7.83 | ksi |
|
抗磨損性 4 | 25.0 | mm3 | ISO 4649 |
撕裂強度 5 (73°F) | 540 | lbf/in | ISO 34-1 |
壓縮永久變形 |
|
| ISO 815 |
73°F, 72 hr | 21 | % |
|
158°F, 24 hr 4 | 42 | % |
|
158°F, 24 hr 6 | 25 | % |
|
Rebound Resilience | 29 | % | ISO 4662 |
干燥溫度 | < 176 | °F |
|
加工（熔體）溫度 | 419 到 455 | °F |
|
模具溫度 | 68 到 104 | °F |
|
干燥溫度 | < 176 | °F |
|
熔體溫度 | 356 到 392 | °F |
|
如需科思創原廠物性表及相關文件，請聯系我們工作人員，謝謝！