ForTii? Ace MX53
Polyamide 4T
產(chǎn)品說(shuō)明:
50% Glass Reinforced, Stable to heat, for Automotive applications
Special Features:
Used In:
ForTii? is a breakthrough high temperature polyamide with halogen-free flame retardant grades for demanding applications in the electronics, lighting, automotive, white goods, industrial and aerospace industries.
We developed ForTii? in close co-operation with leading OEMs and tier 1 connector and socket manufacturers to ensure we give our customer what they want €" and need.
That means a high temperature polyamide with a broad and versatile portfolio of grades that deliver high performance with a unique balance of properties.
填料/增強(qiáng)材料 | 玻璃纖維增強(qiáng)材料, 50% 填料按重量
|
添加劑 | |
特性 | |
加工方法 | |
樹(shù)脂ID (ISO 1043) | |
密度 | 1.64 | g/cm3 | ISO 1183 |
吸水率 (平衡, 73°F, 50% RH) | 1.4 | % | ISO 62 |
拉伸模量 |
|
| ISO 527-2 |
-- | 2.61E+6 | psi |
|
248°F | 2.32E+6 | psi |
|
302°F | 1.67E+6 | psi |
|
320°F | 1.45E+6 | psi |
|
356°F | 1.16E+6 | psi |
|
392°F | 1.04E+6 | psi |
|
拉伸應(yīng)力 |
|
| ISO 527-2 |
斷裂 | 36300 | psi |
|
斷裂, 248°F | 24700 | psi |
|
斷裂, 302°F | 18900 | psi |
|
斷裂, 320°F | 17400 | psi |
|
斷裂, 356°F | 14500 | psi |
|
斷裂, 392°F | 12300 | psi |
|
拉伸應(yīng)變 |
|
| ISO 527-2 |
斷裂 | 2.0 | % |
|
斷裂, 248°F | 2.1 | % |
|
斷裂, 302°F | 3.4 | % |
|
斷裂, 320°F | 4.1 | % |
|
斷裂, 356°F | 4.9 | % |
|
斷裂, 392°F | 5.0 | % |
|
簡(jiǎn)支梁缺口沖擊強(qiáng)度 |
|
| ISO 179/1eA |
-22°F | 6.2 | ft·lb/in2 |
|
73°F | 5.7 | ft·lb/in2 |
|
簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度 |
|
| ISO 179/1eU |
-22°F | 36 | ft·lb/in2 |
|
73°F | 38 | ft·lb/in2 |
|
熱變形溫度 |
|
|
|
66 psi, 未退火 | 626 | °F | ISO 75-2/B |
264 psi, 未退火 | 608 | °F | ISO 75-2/A |
熔融溫度 2 | 635 | °F | ISO 11357-3 |
干燥溫度 | 212 到 266 | °F |
|
干燥時(shí)間 | 2.0 到 4.0 | hr |
|
料筒后部溫度 | 608 到 644 | °F |
|
料筒中部溫度 | 626 到 662 | °F |
|
料筒前部溫度 | 626 到 662 | °F |
|
射嘴溫度 | 644 到 698 | °F |
|
加工（熔體）溫度 | 644 到 698 | °F |
|
模具溫度 | 176 到 392 | °F |
|
注射速度 | 中等偏快 |
|
|
背壓 | 72.5 到 435 | psi |
|
螺桿壓縮比 | 2.5:1.0 |
|
|