ForTii? MX2
Polyamide 4T
產(chǎn)品說(shuō)明:
40% Glass Reinforced, Heat Stabilized, for Automotive applications
Special Features:
Used In:
ForTii? is a breakthrough high temperature polyamide with halogen-free flame retardant grades for demanding applications in the electronics, lighting, automotive, white goods, industrial and aerospace industries.
We developed ForTii? in close co-operation with leading OEMs and tier 1 connector and socket manufacturers to ensure we give our customer what they want €" and need.
That means a high temperature polyamide with a broad and versatile portfolio of grades that deliver high performance with a unique balance of properties.
填料/增強(qiáng)材料 | |
添加劑 | |
特性 | |
用途 | |
加工方法 | |
樹(shù)脂ID (ISO 1043) | |
密度 | 1.55 | -- | g/cm3 | ISO 1183 |
收縮率 |
|
|
| ISO 294-4 |
橫向流量 | 1.0 | -- | % |
|
流量 | 0.35 | -- | % |
|
吸水率 (平衡, 73°F, 50% RH) | 1.8 | -- | % | ISO 62 |
拉伸模量 |
|
|
| ISO 527-2 |
-- | 2.10E+6 | 2.10E+6 | psi |
|
248°F | 1.45E+6 | -- | psi |
|
302°F | 957000 | -- | psi |
|
320°F | 899000 | -- | psi |
|
356°F | 841000 | -- | psi |
|
392°F | 798000 | -- | psi |
|
拉伸應(yīng)力 |
|
|
| ISO 527-2 |
斷裂 | 33400 | 31900 | psi |
|
斷裂, 248°F | 20300 | -- | psi |
|
斷裂, 302°F | 15200 | -- | psi |
|
斷裂, 320°F | 14100 | -- | psi |
|
斷裂, 356°F | 12300 | -- | psi |
|
斷裂, 392°F | 11300 | -- | psi |
|
拉伸應(yīng)變 |
|
|
| ISO 527-2 |
斷裂 | 2.1 | 2.0 | % |
|
斷裂, 248°F | 4.5 | -- | % |
|
斷裂, 302°F | 6.7 | -- | % |
|
斷裂, 320°F | 7.0 | -- | % |
|
斷裂, 356°F | 7.0 | -- | % |
|
斷裂, 392°F | 7.0 | -- | % |
|
簡(jiǎn)支梁缺口沖擊強(qiáng)度 |
|
|
| ISO 179/1eA |
-22°F | 5.2 | 4.8 | ft·lb/in2 |
|
73°F | 5.2 | 4.8 | ft·lb/in2 |
|
簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度 |
|
|
| ISO 179/1eU |
-22°F | 29 | 26 | ft·lb/in2 |
|
73°F | 33 | 29 | ft·lb/in2 |
|
熱變形溫度 |
|
|
|
|
66 psi, 未退火 | 603 | -- | °F | ISO 75-2/B |
264 psi, 未退火 | 581 | -- | °F | ISO 75-2/A |
熔融溫度 2 | 617 | -- | °F | ISO 11357-3 |
線形熱膨脹系數(shù) |
|
|
| ASTM D696 |
流動(dòng) | 1.7E-5 | -- | in/in/°F |
|
橫向 | 1.9E-5 | -- | in/in/°F |
|
體積電阻率 | > 1.0E+15 | > 1.0E+15 | ohms·cm | IEC 60093 |
相對(duì)電容率 |
|
|
| IEC 60250 |
100 Hz | 4.90 | 5.70 |
|
|
1 MHz | 4.60 | 4.80 |
|
|
耗散因數(shù) |
|
|
| IEC 60250 |
100 Hz | 5.7E-3 | 0.027 |
|
|
1 MHz | 0.018 | 0.029 |
|
|
干燥溫度 | 212 | °F |
|
干燥時(shí)間 | 2.0 | hr |
|
料筒后部溫度 | 608 到 626 | °F |
|
料筒中部溫度 | 617 到 644 | °F |
|
料筒前部溫度 | 626 到 653 | °F |
|
射嘴溫度 | 626 到 653 | °F |
|
加工（熔體）溫度 | 626 到 662 | °F |
|
模具溫度 | 212 到 302 | °F |
|
注射速度 | 中等偏快 |
|
|
背壓 | 72.5 到 435 | psi |
|
螺桿壓縮比 | 2.5:1.0 |
|
|