產品說明:
Ultramid A3WG10 is a 50% glass fiber reinforced and heat aging resistance injection molding PA66 grade.
Applications
Typical applications include industrial articles having very high rigidity.
填料/增強材料 | 玻璃纖維增強材料, 50% 填料按重量 |
特性 | 剛性，高、良好的耐熱老化性能、耐油性能 |
用途 | 工業(yè)應用 |
機構評級 | EC 1907/2006 (REACH) |
RoHS 合規(guī)性 | RoHS 合規(guī) |
形式 | 粒子 |
加工方法 | 注射成型 |
多點數據 | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2) |
密度 / 比重 |
|
|
|
|
-- | 1.55 | -- |
| ASTM D792 |
-- | 1.55 | -- | g/cm3 | ISO 1183 |
熔融體積流量（MVR） (275°C/5.0 kg) | 1.22 | -- | in3/10min | ISO 1133 |
收縮率 - 流動 (0.125 in) | 1.0E-3 | -- | in/in |
|
吸水率 |
|
|
|
|
飽和 | 4.0 | -- | % | ASTM D570 |
飽和, 73°F | 4.0 | -- | % | ISO 62 |
平衡, 50% RH | 1.2 | -- | % | ASTM D570 |
平衡, 73°F, 50% RH | 1.2 | -- | % | ISO 62 |
拉伸模量 (73°F) | 2.44E+6 | 1.81E+6 | psi | ISO 527-2 |
抗張強度 |
|
|
|
|
斷裂, 73°F | 33400 | -- | psi | ASTM D638 |
斷裂, 73°F | 33400 | 26100 | psi | ISO 527-2 |
斷裂, 176°F | 21900 | 16400 | psi | ISO 527-2 |
伸長率 |
|
|
|
|
斷裂, 73°F | 2.0 | -- | % | ASTM D638 |
斷裂, 73°F | 2.5 | 3.5 | % | ISO 527-2 |
斷裂, 176°F | 5.2 | 4.9 | % | ISO 527-2 |
彎曲模量 |
|
|
|
|
73°F | 1.70E+6 | -- | psi | ASTM D790 |
73°F | 2.18E+6 | -- | psi | ISO 178 |
簡支梁缺口沖擊強度 |
|
|
| ISO 179 |
-22°F | 6.2 | -- | ft·lb/in2 |
|
73°F | 8.6 | 12 | ft·lb/in2 |
|
簡支梁無缺口沖擊強度 |
|
|
| ISO 179 |
-22°F | 40 | -- | ft·lb/in2 |
|
73°F | 45 | 48 | ft·lb/in2 |
|
懸壁梁缺口沖擊強度 |
|
|
| ASTM D256 |
-40°F | 1.9 | -- | ft·lb/in |
|
73°F | 2.5 | -- | ft·lb/in |
|
載荷下熱變形溫度 |
|
|
|
|
66 psi, 未退火 | 482 | -- | °F | ASTM D648, ISO 75-2/B |
264 psi, 未退火 | 482 | -- | °F | ASTM D648, ISO 75-2/A |
熔融峰值溫度 | 500 | -- | °F | ASTM D3418, ISO 3146 |
線形熱膨脹系數 |
|
|
|
|
流動 | 3.9E-6 | -- | in/in/°F | ASTM E831 |
流動 | 7.2E-6 | -- | in/in/°F |
|
橫向 | 3.1E-5 | -- | in/in/°F |
|
RTI Elec |
|
|
| UL 746 |
0.031 in | 257 | -- | °F |
|
0.06 in | 257 | -- | °F |
|
0.12 in | 257 | -- | °F |
|
RTI Imp |
|
|
| UL 746 |
0.06 in | 266 | -- | °F |
|
0.12 in | 266 | -- | °F |
|
RTI |
|
|
| UL 746 |
0.06 in | 266 | -- | °F |
|
0.12 in | 266 | -- | °F |
|
體積電阻率 |
|
|
|
|
0.0591 in | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
-- | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
介電常數 (1 MHz) | 3.80 | 6.60 |
| IEC 60250 |
耗散因數 |
|
|
| IEC 60250 |
100 Hz | 0.015 | 0.17 |
|
|
1 MHz | 0.015 | 0.30 |
|
|
漏電起痕指數 | 450 | 450 | V | IEC 60112 |
UL 阻燃等級 |
|
|
| UL 94 |
0.031 in | HB | -- |
|
|
0.06 in | HB | -- |
|
|
0.12 in | HB | -- |
|
|
干燥溫度 | 176 | °F |
|
干燥時間 | 2.0 到 4.0 | hr |
|
建議的最大水分含量 | 0.15 | % |
|
加工（熔體）溫度 | 536 到 581 | °F |
|
模具溫度 | 176 到 194 | °F |
|
注塑壓力 | 500 到 1500 | psi |
|
注射速度 | 快速 |
|
|